beusi tuang Manual éléktroda ENi-Cl barang las
KOMPONEN KIMIA:
| PADUNGAN (wt%) | C | Mn | Si | Ni | Fe | Al | Cu | P | S |
| ATURAN GB/T | 2.00 | 1.00 | 2.50 | ≥90 | 8.00 | - | - | - | 0.03 |
| ATURAN AWS | 2.00 | 2.50 | 4.00 | ≥85 | 8.00 | 1.00 | 2.50 | - | 0.03 |
| NILAI CONTOH | 0.23 | 0.16 | 0.97 | 97.2 | 1.1 | 0.24 | 0.01 | 0,024 | 0.003 |
PILIHAN MEKANIKAL:
| HARTA | Kakuatan ngahasilkeun (MPa) | Kakuatan éksténsif (MPa) | NILAI IMPAK J/℃ | ELONGATION(%) | ||||
| ATURAN GB/T | - | - | - | - | ||||
| ATURAN AWS | - | - | - | - | ||||
| NILAI CONTOH | - | - | - | - | ||||
Parameter las anu disarankeun:
| SPESIFIKASI DIAMETER (mm) | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | ||||
| LISTRIK (Amp) | H/W | 60-80 | 70-120 | 100-150 | 130-170 | |||
éléktroda mangrupa inti nikel murni, kuat graphitized éléktroda beusi tuang;
Nalika las, weldment teu bisa preheated;
The las rod mangrupakeun jenis beusi rod las tiis kalawan kinerja komprehensif hadé kayaning résistansi retakan, sipat machining, operability las sarta sipat mékanis.
-
CJ50 jack-up pangeboran rig
-
Mei Jin Hua Sheng étiléna glikol munara sintétik
-
3000m platform pangeboran semi-submersible jero cai "Haiyang Shiyou 981"
KOMPONEN KIMIA:
| PADUNGAN (wt%) | C | Mn | Si | Ni | Fe | Al | Cu | P | S |
| ATURAN GB/T | 2.00 | 1.00 | 2.50 | ≥90 | 8.00 | - | - | - | 0.03 |
| ATURAN AWS | 2.00 | 2.50 | 4.00 | ≥85 | 8.00 | 1.00 | 2.50 | - | 0.03 |
| NILAI CONTOH | 0.23 | 0.16 | 0.97 | 97.2 | 1.1 | 0.24 | 0.01 | 0,024 | 0.003 |
PILIHAN MEKANIKAL:
| HARTA | Kakuatan ngahasilkeun (MPa) | Kakuatan éksténsif (MPa) | NILAI IMPAK J/℃ | ELONGATION(%) | ||||
| ATURAN GB/T | - | - | - | - | ||||
| ATURAN AWS | - | - | - | - | ||||
| NILAI CONTOH | - | - | - | - | ||||
Parameter las anu disarankeun:
| SPESIFIKASI DIAMETER (mm) | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | ||||
| LISTRIK (Amp) | H/W | 60-80 | 70-120 | 100-150 | 130-170 | |||