beusi tuang Manual éléktroda ENiFe-Cl las asesoris
KOMPONEN KIMIA:
| PADUNGAN (wt%) | C | Mn | Si | Cr | Fe | Al | Cu | P | S |
| ATURAN GB/T | 2.00 | 2.50 | 4.00 | 45-60 | Margin | 1.00 | 2.50 | - | 0.03 |
| ATURAN AWS | 2.00 | 2.50 | 4.00 | 45-60 | Margin | 1.00 | 2.50 | - | 0.03 |
| NILAI CONTOH | 0.59 | 0.26 | 0.93 | 55.1 | 42.8 | 0.18 | 0.03 | 0,023 | 0,005 |
PILIHAN MEKANIKAL:
| HARTA | Kakuatan ngahasilkeun (MPa) | Kakuatan éksténsif (MPa) | NILAI IMPAK J/℃ | ELONGATION(%) | ||||
| ATURAN GB/T | - | - | - | - | ||||
| ATURAN AWS | - | - | - | - | ||||
| NILAI CONTOH | - | - | - | - | ||||
Parameter las anu disarankeun:
| SPESIFIKASI DIAMETER (mm) | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | ||||
| LISTRIK (Amp) | H/W | 60-80 | 80-120 | 120-150 | 130-180 | |||
Éléktroda nyaéta kawat inti nikel, éléktroda beusi tuang graphitized kuat.
Nalika las, weldment teu bisa preheated.
Cai mibanda ciri kakuatan tinggi, plasticity alus, résistansi cracking alus teuing jeung fusi alus kalawan logam dasar.
-
Cina Élmu & Téhnologi Co., LTD. 20 juta ton / taun proyék pemurnian jeung integrasi kimiawi
-
Bahan las pikeun wadahna
Shaanxi Pucheng -50 ℃ proyék tank buleud propana
KOMPONEN KIMIA:
| PADUNGAN (wt%) | C | Mn | Si | Cr | Fe | Al | Cu | P | S |
| ATURAN GB/T | 2.00 | 2.50 | 4.00 | 45-60 | Margin | 1.00 | 2.50 | - | 0.03 |
| ATURAN AWS | 2.00 | 2.50 | 4.00 | 45-60 | Margin | 1.00 | 2.50 | - | 0.03 |
| NILAI CONTOH | 0.59 | 0.26 | 0.93 | 55.1 | 42.8 | 0.18 | 0.03 | 0,023 | 0,005 |
PILIHAN MEKANIKAL:
| HARTA | Kakuatan ngahasilkeun (MPa) | Kakuatan éksténsif (MPa) | NILAI IMPAK J/℃ | ELONGATION(%) | ||||
| ATURAN GB/T | - | - | - | - | ||||
| ATURAN AWS | - | - | - | - | ||||
| NILAI CONTOH | - | - | - | - | ||||
Parameter las anu disarankeun:
| SPESIFIKASI DIAMETER (mm) | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | ||||
| LISTRIK (Amp) | H/W | 60-80 | 80-120 | 120-150 | 130-180 | |||