Low-Alloy Steels Manual éléktroda E7016-C2L Kasalametan tank suntik Consumables
Komposisi utama nyaéta 3,5% baja Ni, rod las leungeun tipe kalium hidrogén low, dina suhu operasi -75C, lebur na
Dampak kateguhan logam anu alus teuing
arc stabil, kirang Santika, molding alus, panyabutan slag gampang, kinerja X-Rav téh alus teuing.
KOMPONEN KIMIA:
PADUNGAN (wt%) | C | Si | Mn | P | S | Ni | Cr | Mo | Lain | |
ATURAN GB/T | 0.046 | 0.25 | 0.72 | 0.009 | 0.007 | 3.5 | 0.033 | 0.01 | - |
SIFAT MEKANIKAL:
HARTA | Kakuatan ngahasilkeun (MPa) | Kakuatan éksténsif (MPa) | Elongation(%) | NILAI IMPAK J/℃ | Perlakuan panas °C*h | |||||
ATURAN GB/T | 495 | 595 | 27 | 75/-75 | 620*1 |
Parameter las anu disarankeun:
SPESIFIKASI DIAMETER (mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | |||||
LISTRIK (Amp) | H/W | 70-100 | 100-140 | 140-180 | 180-230 | ||||
O/W | 60-90 | 90-130 | 120-160 | - |
-
Shandong Zibo Haiyi 8 sét 3000m³ propiléna spherical tank
-
300.000 ton lepas pantai Floating Storage Storage Tanker (FPSO)
-
Hainan Huasheng
munara recovery fénol
KOMPONEN KIMIA:
PADUNGAN (wt%) | C | Si | Mn | P | S | Ni | Cr | Mo | Lain | |
ATURAN GB/T | 0.046 | 0.25 | 0.72 | 0.009 | 0.007 | 3.5 | 0.033 | 0.01 | - |
SIFAT MEKANIKAL:
HARTA | Kakuatan ngahasilkeun (MPa) | Kakuatan éksténsif (MPa) | Elongation(%) | NILAI IMPAK J/℃ | Perlakuan panas °C*h | |||||
ATURAN GB/T | 495 | 595 | 27 | 75/-75 | 620*1 |
Parameter las anu disarankeun:
SPESIFIKASI DIAMETER (mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | |||||
LISTRIK (Amp) | H/W | 70-100 | 100-140 | 140-180 | 180-230 | ||||
O/W | 60-90 | 90-130 | 120-160 | - |