Low-Alloy Steels Manual Éléktroda E8016-C4 Mod jack-up rigs Consumables
Komponén utama nyaéta 1,5% Ni, éléktroda leungeun tipe kalium hidrogén low, dina suhu operasi -50C, kateguhan dampak tina logam disimpen téh alus teuing.
arc stabil, kirang Santika, molding alus, panyabutan slag gampang
Kinerja X-Ray alus teuing.
KOMPONEN KIMIA:
PADUNGAN (wt%) | C | Si | Mn | P | S | Ni | Cr | Mo | Lain | |
ATURAN GB/T | 0,082 | 0.42 | 1.07 | 0.009 | 0.007 | 1.49 | 0,025 | 0,005 | - |
SIFAT MEKANIKAL:
HARTA | Kakuatan ngahasilkeun (MPa) | Kakuatan éksténsif (MPa) | Elongation(%) | NILAI IMPAK J/℃ | Perlakuan panas °C*h | |||||
ATURAN GB/T | 505 | 600 | 23 | 105/-50 | 620*1 |
Parameter las anu disarankeun:
SPESIFIKASI DIAMETER (mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | |||||
LISTRIK (Amp) | H/W | 70-100 | 100-140 | 140-180 | 180-230 | ||||
O/W | 60-90 | 90-130 | 120-160 | - |
Daya Nuklir Sanmen
-
JU2000E jack-up pangeboran platform
Harbin listrik tilu Gerbang CMT
KOMPONEN KIMIA:
PADUNGAN (wt%) | C | Si | Mn | P | S | Ni | Cr | Mo | Lain | |
ATURAN GB/T | 0,082 | 0.42 | 1.07 | 0.009 | 0.007 | 1.49 | 0,025 | 0,005 | - |
SIFAT MEKANIKAL:
HARTA | Kakuatan ngahasilkeun (MPa) | Kakuatan éksténsif (MPa) | Elongation(%) | NILAI IMPAK J/℃ | Perlakuan panas °C*h | |||||
ATURAN GB/T | 505 | 600 | 23 | 105/-50 | 620*1 |
Parameter las anu disarankeun:
SPESIFIKASI DIAMETER (mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | |||||
LISTRIK (Amp) | H/W | 70-100 | 100-140 | 140-180 | 180-230 | ||||
O/W | 60-90 | 90-130 | 120-160 | - |