alloy nikel TIG ERNiCrMo-3 bahan Soldering
KOMPONEN KIMIA:
| PADUNGAN (wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
| ATURAN GB/T | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.0-4.2 | - | - |
| ATURAN AWS | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.15-4.15 | 0.02 | 0,015 |
| NILAI CONTOH | 0.006 | 0.15 | 0.12 | 22.02 | 64.84 | 8.75 | 0.18 | 3.49 | 0.001 | 0.001 |
PILIHAN MEKANIKAL:
| HARTA | Kakuatan ngahasilkeun (MPa) | Kakuatan éksténsif (MPa) | NILAI IMPAK J/℃ | ELONGATION(%) | ||||
| ATURAN GB/T | - | - | - | - | ||||
| ATURAN AWS | - | - | - | - | ||||
| NILAI CONTOH | - | 790 | 159/-196 | 46 | ||||
Nikel-kromium-molybdenum nikel-base alloy gas kawat las, komposisi nominal nyaeta 61% Ni-22% Cr-9% Mo-3.5% Nb + Ta.
Logam molten gaduh sipat mékanis anu saé sareng résistansi anu hadé pikeun korosi pitting sareng korosi crevice.
Arc stabil, ngabentuk geulis, aliran alus beusi molten, kalawan kinerja prosés las alus teuing.
KOMPONEN KIMIA:
| PADUNGAN (wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
| ATURAN GB/T | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.0-4.2 | - | - |
| ATURAN AWS | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.15-4.15 | 0.02 | 0,015 |
| NILAI CONTOH | 0.006 | 0.15 | 0.12 | 22.02 | 64.84 | 8.75 | 0.18 | 3.49 | 0.001 | 0.001 |
PILIHAN MEKANIKAL:
| HARTA | Kakuatan ngahasilkeun (MPa) | Kakuatan éksténsif (MPa) | NILAI IMPAK J/℃ | ELONGATION(%) | ||||
| ATURAN GB/T | - | - | - | - | ||||
| ATURAN AWS | - | - | - | - | ||||
| NILAI CONTOH | - | 790 | 159/-196 | 46 | ||||
Tulis pesen anjeun di dieu sareng kirimkeun ka kami