alloy nikel Flux cored kawat ENiCrMo3T1-4 sambungan Soldering
KOMPONEN KIMIA:
| PADUNGAN (wt%) | C | Mn | Si | Cr | Ni | Fe | Nb | Mo | P | S |
| ATURAN GB/T | - | - | - | - | - | - | - | - | - | - |
| ATURAN AWS | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58.0 | 5.00 | 3.15-4.15 | 8.0-10.0 | 0.02 | 0.02 |
| NILAI CONTOH | 0,015 | 0.25 | 0.3 | 22 | 64.00 | 0.3 | 3.3 | 9.5 | 0.0005 | 0.0005 |
SIFAT MEKANIKAL:
| HARTA | Kakuatan ngahasilkeun (MPa) | Kakuatan éksténsif (MPa) | NILAI IMPAK J/℃ | ELONGATION(%) | ||||
| ATURAN GB/T | - | - | - | - | ||||
| ATURAN AWS | - | 690 | - | 25 | ||||
| NILAI CONTOH | - | 760 | 80/-196 | 32 | ||||
Parameter las anu disarankeun:
| SPESIFIKASI DIAMETER (mm) | 1.2 | ||||
| Volt | 25-34 | ||||
| Amp | 150-250 | ||||
| Panjang extension garing (mm) | 15-25 | ||||
| Aliran gas (l/mnt) | 20-25 | ||||
Komposisi nominal éta 60% Ni-22% Cr-9% Mo-3% Fe-3.6% Nb.
-196 ° C kinerja dampak suhu low téh alus teuing.
busur lemes jeung stabil, kirang Santika, ngabentuk geulis, panyabutan slag alus, feed kawat stabil, kalawan kinerja prosés las alus teuing.
-
Aplikasi kakuatan termal
-
Ladang Minyak Qinghai Youjian Wunan
-
20000 TEU kapal wadahna
KOMPONEN KIMIA:
| PADUNGAN (wt%) | C | Mn | Si | Cr | Ni | Fe | Nb | Mo | P | S |
| ATURAN GB/T | - | - | - | - | - | - | - | - | - | - |
| ATURAN AWS | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58.0 | 5.00 | 3.15-4.15 | 8.0-10.0 | 0.02 | 0.02 |
| NILAI CONTOH | 0,015 | 0.25 | 0.3 | 22 | 64.00 | 0.3 | 3.3 | 9.5 | 0.0005 | 0.0005 |
SIFAT MEKANIKAL:
| HARTA | Kakuatan ngahasilkeun (MPa) | Kakuatan éksténsif (MPa) | NILAI IMPAK J/℃ | ELONGATION(%) | ||||
| ATURAN GB/T | - | - | - | - | ||||
| ATURAN AWS | - | 690 | - | 25 | ||||
| NILAI CONTOH | - | 760 | 80/-196 | 32 | ||||
Disarankeun las parameterS:
| SPESIFIKASI DIAMETER (mm) | 1.2 | ||||
| Volt | 25-34 | ||||
| Amp | 150-250 | ||||
| Panjang extension garing (mm) | 15-25 | ||||
| Aliran gas (l/mnt) | 20-25 | ||||